In this article, a 0.7 nm thick monolayer MoS2nanosheet gate-all-around field effect transistors (NS-GAAFETs) with conformal high-κmetal gate deposition are demonstrated. The device with 40 nm channel length exhibits a high on-state current density of ~410µAµm-1with a large on/off ratio of 6 × 108at drain voltage = 1 V. The extracted contact resistance is 0.48 ± 0.1 kΩµm in monolayer MoS2NS-GAAFETs, thereby showing the channel-dominated performance with the channel length scaling from 80 to 40 nm. The successful demonstration of device performance in this work verifies the integration potential of transition metal dichalcogenides for future logic transistor applications.
RESUMO
Because of the intrinsic low carrier density of monolayer two-dimensional (2D) materials, doping is crucial for the performance of underlap top-gated 2D devices. However, wet etching of a high-k (dielectric constant) dielectric layer is difficult to implement without causing performance deterioration on the devices; therefore, finding a suitable spacer doping technique for 2D devices is indispensable. In this study, we developed a remote doping (RD) method in which defective SiOx can remotely dope the underlying high-k capped 2D regions without directly contacting these materials. This method achieved a doping density as high as 1.4 × 1013 cm-2 without reducing the mobility of the doped materials; after 1 month, the doping concentration remained as high as 1.2 × 1013 cm-2. Defective SiOx can be used to dope most popular 2D transition-metal dichalcogenides. The low-k properties of SiOx render it ideal for spacer doping, which is very attractive from the perspective of circuit operation. In our experiments, MoS2 and WS2 underlap top-gate devices exhibited 10× and 200× increases in their on-currents, respectively, after being doped with SiOx. These results indicate that SiOx doping can be conducted to manufacture high-performance 2D devices.